Acrylnitril-Butadien-Styrol (ABS)

Mixed regenerate from Acrylnitril-Butadien-Styrol without differentiating between various types of ABS coloured in one neutral colour:

  • Mecanical properties
    thensile strength at yield:
    ISO 527  /  Mpa  /  34
    elongation at yield stress:
    ISO 527  /  %  /  4
    tensile strength:
    ISO 527  /  MPa  /  33
    elongation at break:
    ISO 527  /  %  /  25
    E-module (4 Pt. bending test):
    EN ISO 178  /  MPa  /  2200
    limiting bending stress:
    DIN 53452  /  MPa  /  45
    impact strength at 23 °C:
    EN ISO 179/1eU  /  kj/m2  /  >35
    impact strength at -30 °C:
    EN ISO 179/1eU  /  kj/m131  /  25
    notched impact strength at 23 °C:
    EN ISO 179/1eA  /  kj/m132  /  6
    notched impact strength at -30 °C:
    EN ISO 179/1eA  /  kj/m133  /  5
    ball hardness (H 358/30):
    EN ISO 2039-1  /  N/mm2
  • Thermal properties
    Vicat softenung temperature VST B 50:
    ISO 306  /  °C  /  90
    ISO/R75 method A:
    ISO75  /  °C
    ISO/R75 method B:
    ISO75  /  °C
    continuous operating temperature:
    °C  /  70
    linear thermal expansion coefficient:
    ISO 7991  /  10^-5/K
    thermal conductivity:
    ISO 8302  /  W/Km
  • Electrical properties
    dielectric constant:
    IEC 250
    dielectric loss factor:
    IEC 250  /  10^-4
    contact resistence:
    DIN EN 61340-5-1  /  Ω cm
    surface resistence:
    DIN EN 61340-5-2  /  Ω
    dielectric strength:
    VDE 0303  /  kV/mm
  • Other properties
    processing speed:
    %
    water absorption:
    ISO 62  /  %
    explosive density (nature):
    ISO 1183  /  g/cm3  /  1,02-1,12

  Download as PDF

conductive Polystyrene (PS ESD)

Mixed regenerate from Polystyrene without differentiating between various types of PS coloured in one neutral colour:

  • Mecanical properties
    tensile strength at yield:
    ISO 527  /  Mpa  /  34
    elongation at yield stress:
    ISO 527  /  %  /  4
    tensile strength:
    ISO 527  /  MPa  /  22
    elongation at break:
    ISO 527  /  %  /  4
    E-module (4 Pt. bending test):
    EN ISO 178  /  MPa  /  2200
    limiting bending stress:
    DIN 53452  /  MPa  /  45
    impact strength at 23°C:
    EN ISO 179/1eU  /  kj/m2  /  >35
    impact strength at -30 °C:
    EN ISO 179/1eU  /  kj/m131  /  25
    notched impact strength at 23 °C:
    EN ISO 179/1eA  /  kj/m132  /  10
    notched impact strength at -30 °C:
    EN ISO 179/1eA  /  kj/m133  /  5
    ball hardness (H 358/30):
    EN ISO 2039-1  /  N/mm2
  • Thermal properties
    Vicat softening temperature VST B 50:
    ISO 306  /  °C  /  90
    ISO/R75 method A:
    ISO75  /  °C
    ISO/R75 method B:
    ISO75  /  °C
    continuous operating temperature:
    °C  /  70
    linear thermal expansion coefficient:
    ISO 7991  /  10^-5/K
    thermal conductivity:
    ISO 8302  /  W/Km
  • Electrical properties
    dielectric constant:
    IEC 250
    dielectric loss factor:
    IEC 250  /  10^-4
    contact resistence:
    DIN EN 61340-5-1  /  Ω cm  /  <10^3
    surface resistence:
    DIN EN 61340-5-2  /  Ω  /  <10^4
    explosive density (nature):
    VDE 0303  /  kV/mm
  • Other properties
    processing speed:
    %
    water absorption:
    ISO 62  /  %
    explosive density (nature):
    ISO 1183  /  g/cm3  /  1,02-1,12

  Download as PDF

regenerated Polystyrene (PS)

Mixed regenerate from Polystyrene without differentiating between various types of PS coloured in one neutral colour:

  • Mecanical properties
    tensile strength at yield:
    ISO 527  /  Mpa  /  34
    elongation at yield stress:
    ISO 527  /  %  /  4
    tensile strength:
    ISO 527  /  MPa  /  22
    elongation at break:
    ISO 527  /  %  /  4
    E-module (4 Pt. bending test):
    EN ISO 178  /  MPa  /  2200
    limiting bending stress:
    DIN 53452  /  MPa  /  45
    impact strength at 23°C:
    EN ISO 179/1eU  /  kj/m2  /  >35
    impact strength at -30 °C:
    EN ISO 179/1eU  /  kj/m131  /  25
    notched impact strength at 23 °C:
    EN ISO 179/1eA  /  kj/m132  /  10
    notched impact strength at -30 °C:
    EN ISO 179/1eA  /  kj/m133  /  5
    ball hardness (H 358/30):
    EN ISO 2039-1  /  N/mm2
  • Thermal properties
    Vicat softening temperature VST B 50:
    ISO 306  /  °C  /  90
    ISO/R75 method A:
    ISO75  /  °C
    ISO/R75 method B:
    ISO75  /  °C
    continuous operating temperature:
    °C  /  70
    linear thermal expansion coefficient:
    ISO 7991  /  10^-5/K
    thermal conductivity:
    ISO 8302  /  W/Km
  • Electrical properties
    dielectric constant:
    IEC 250
    dielectric loss factor:
    IEC 250  /  10^-4
    contact resistence:
    DIN EN 61340-5-1  /  Ω cm
    surface resistence:
    DIN EN 61340-5-2  /  Ω
    dielectric strength:
    VDE 0303  /  kV/mm
  • Other properties
    processing speed:
    %
    water absorption:
    ISO 62  /  %
    explosive density (nature):
    ISO 1183  /  g/cm3  /  1,02-1,12

  Download as PDF

The values indicated are minimum values and could significantly vary based on the different ABS products employed. These values are characteristical properties that are not considered to be product specifications. The mechanical properties as used in this technical specification sheet have been established on extruded plate-bodies of 4 mm thickness. The data of this technical specification sheet have been established using great care. We can however not accept any responsibility since products are used in various different applications.

Our program

See all of our products with their technical details.

  Our program

Colours

Our standard and special colours for polystyrene concentrates.

  Colour Chart

Additives

Increased possibilities for our sheet material with increase product quality requirements.

  Additives

Our quality claim as extruders: high value, reliability & fair prices for our customers in europe